Water-Based PVC Coated Overlay Film High adhesion - Smard Card Material for Smart Card lamination
1. Water-Based PVC Coated Overlay Film High adhesion - Smard Card Material - Introduciton
PVC Coated Overlay MCO-W model is suitable for laminating with most PVC sheets printed by various printers. It features high adhesion, no color change and deformation.
It is applicable to almost all sheets printed by various ink. It features excellent peeling strength and long aging time.
2. Water-Based PVC Coated Overlay Film High adhesion - Smard Card Material - Parameters
Technical Parameters:
| Item | Parameters |
| Vicat softening point | 72±2 ℃ |
| Heating Shrinkage ratio | ≤10 % |
| Tensile Strength | ≥40 MPa |
| Normal thickness in mm | 0.04,0.05,0.06,0.08,0.10 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
Parameters:
1). Size: in reel or sheet, A4, A3 or as per customer requirements
2). Normal thickness: 0.04,0.05,0.06,0.08,0.10mm
3). Color: transparent with one-side glue coating.
4). Package method: by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet.
5). Storage condition: Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight.
3. Water-Based PVC Coated Overlay Film High adhesion - Smard Card Material - Application
Brief Introduction:
PVC Coated Overlay is suitable for laminating with conventional ink and UV ink. It could reach excellent peel strength as using Water Based Laminating Varnish . It provides superior aging resistance performance to other similar products, no color change and deformation after lamination. Laserable Coated Overlay is also offered.
Characteristics:
● Suitable for conventional ink and UV ink, excellent peel strength even with pearl ,gold ,silver and dark color inks.
● Keep the fluorescent anti-forgery mark clearly.
● Non-Sticky and easy for magnetic stripe tape-laying.
● Abrasion resistant , prolong the life of cards.
● Environment friendly, no solvent or gas discharged.
Technical Parameters:
| Item | Parameters |
| Vicat (℃) | 72±2 ℃ |
| Shrinkage (%) | ≤10% |
| Tensile Strength (MPa) | MD | ≥40 |
| TD | ≥35 |
| Roughness (μm) | Ra | 0.5~1.8 |
| Rz | 3~9 |
| Thickness (mm) | 0.04~0.1 |
◆Product Category and Laminating Condition:
| Product Category | MCO-W |
| Application | ID Card,Social Security Card,Bank Card,etc | Bank Card,Shopping Card,etc | Membership Card,Commercial Card,etc |
| Suggested Laminating Condition | Laminating Unit | Heat Laminating | Cool Laminating | Heat Laminating | Cool Laminating | Heat Laminating | Cool Laminating |
| Temp | 130~150℃ | ≤25℃ | 130~150℃ | ≤25℃ | 135~155℃ | ≤25℃ |
| Time | 25min | 15 min | 25min | 15 min | 25min | 15 min |
| Pressure | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa |
4. Water-Based PVC Coated Overlay Film High adhesion - Smard Card Material - Packing
Packing:
Outside:Carton Inside:PE bag
Storage:
Keep package sealed and moisture-proof , room temperature under 40℃.
Stacking height should not exceed one meter.
Keep horizontally, avoid oppress heavily and direct sun light.
Shelf life: Two years.