0.10mm PETG Plastic Sheet Anti Static Impact Resistance For ID Card Production Material
1. Introduction of 0.10mm PETG Plastic Sheet Anti Static Impact Resistance For ID Card Production Material
0.10mm PETG Plastic Sheet Anti Static Impact Resistance is widely used in card base production. It has such features as impact resistance, high temperature resistance, anti-static, abrasion, folding and high strength. It is widely used for the production of high-end credit cards, ID cards and passport, etc.
PETG is a kind of transparent amorphous copolyester.
The performance of PETG is quite different from PET and PC. PETG plate has outstanding toughness and high impact strength, its impact strength is 3-10 times more than ordinary plastic plate, and it has a wide processing range, high mechanical strength and excellent flexibility. Compared with PVC, it has high transparency, good luster and easy to print. At the same time, PETG has environmental protection advantages, and it can be recycled without polluting the environment. PETG sheet has low flammability, good fire resistance, no combustion support, low smoke emission, no harmful substances after combustion.
Card-making method:
1). Print the patterns directly to the material
2). Laminate with overlay
3). Punching
4). Other art-work
2.Specification of 0.10mm PETG Plastic Sheet Anti Static Impact Resistance For ID Card Production Material
0.10mm PETG Plastic Sheet Anti Static Impact Resistance is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection.
Technical Parameters:
| Item | Parameters |
| Vicat softening point (B50) | 78±2 |
| Vicat softening point (A120) | 80±2 |
| Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
| Surface Dyne (dynes/cm) | ≥38 |
| Normal thickness in mm | 0.10-0.76 |
| Density (g/cm3) | 1.30 ±0.05 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
Features:
1).Excellent strength and wear-resisting
2).High temperature and low temperate resistance;
3).Perfect application for laser Engraving
4).Environment-friendly material
5).Longer service life
| Item | PETG Core Sheet |
| Color | White |
| Thickness Range(mm) | 0.1-0.76 |
| Vicat point ℃ | 78-80 ± 2 |
| Tensile strength | ≥50 Mpa |
| Surface | Both sides matt |
| Density | 1.3 ± 0.05 |
| Transparency | ≤5 |
| Heat shrink | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse)
|
3. Application of 0.10mm PETG Plastic Sheet Anti Static Impact Resistance For ID Card Production Material
| Product model | Product name | Thickness Range mm | Color | Vicat ℃ | dynes/cm | Apparent density g/cm3 | Peel strength N/cm | Main application |
| PETG | PETG plastic sheet | 0.1-0.76 | White
| 78-80 | ≥38 | 1.3+/-0.05 | / | It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection. |
Detailed Product Description
1.Thickness:0.1mm to 0.76mm
2.Color: White or customized
3.Surface tension: ≥38 dynes/cm
Characteristic
1.Good lamination properties
2.Good impact resistance
3.Good chemical resistance
4.Excellent printability with either offset or screen printing
5.Laminating Temp 120 degrees Celcius-130 degrees Celcius (lab conditions)
4.Packing of 0.10mm PETG Plastic Sheet Anti Static Impact Resistance For ID Card Production Material
In standard export carton: 50 or 100 or 200 sheets per bag, 10 bags per paper carton, and the cartons are piled up and firmly fixed on solid plywood pallets
Product Tags:
|
|
ID Card Production Anti Static A3 0.10mm Clear PETG Sheet Images
|