White Inkjet Printing PVC Sheet MIP-W is specially used for various inkjet printers such as Epson and Cannon inkjet printer. It could be printed directly by inkjet printers with high definition images.
● High resolution images.
● Excellent ink adhesion, strong peeing strength after lamination with the matching Coated Overlay .
● No crack occurs on the printed images after lamination at high temperature.
Product Features:
Parameters:
1. Size: A4, A3 or as per customer requirements
2. Thickness: 0.15mm-0.40mm
3. Color : White (MIP-W model)/Super White (MIP-SW)
4. Package method: 50 or 100 sheets per bag, 10 bags per paper carton, and the cartons are piled up and firmly fixed on solid plywood pallets.
5. Storage condition: Sealed, moisture-proof, room temperature under 40℃
Size tolerance:+/-0.5 mm in length and width, +/-5% in thickness
1). Low dust
2). Excellent stable quality
3). Exact sheet size cutting and thickness control
4). Low static easy for sheet feeding
5). Smooth roughness
6). Adjustable VICAT degree
7). Adjustable Opaque degree
8). Perfect packaging for transportation
9). Special formulation according to each client's requirement
10). Surface tension can over 40 Dyne
11). Less than15 days Short Lead Time
12). Best after sell service
3.Test Report of 0.33mm White Inkjet Printable PVC Sheets With Strong Peeing Strength
| Product test report |
| Product Name: PVC Digital Printing Sheet |
| Inspected Items | Unit | Inspection Standard | Test Result |
| Appearance | | The color is even,
No black impurity spots,
No obvious scratch | Meet the requirements |
| Length | mm | ±1 | OK |
| Width | mm | ±1 | OK |
| Thickness | mm | ±10% | OK |
| Squareness | mm/m | ≤1 | 0.4 |
| Density | g/cm3 | 1.42±0.05 | 1.41 |
| Chromatic aberration | ∆E | ≤1.0 | 0.51 |
| Pulling Strength | MD | MPa | ≥45 | 47 |
| CD | ≥43 | 43.1 |
Roughness
Ra | 4# | ṷ m | 0.7～1.8 | 1.28 |
| 5# | ṷ m | 0.7～1.8 | 0.97 |
Roughness
Rz | 4# | ṷ m | 4～12 | 7.912 |
| 5# | ṷ m | 4～12 | 6.91 |
| Surface Tension | 4# | Dynes/cm | ≥34 | 34.5 |
| 5# | ≥34 | 34 |
| Heating shrinkage rate | MD | % | ≤-6.0 | -2 |
| CD | ≤+2.2 | 0 |
| Whiteness | | | | 96.2 |
| Transmittance | | % | | 5.5 |
| Vicat softening point | | ℃ | 78±2 | 78.9 |